Titanium CP Grade 12


Technical Data Sheet

Chemical Composition Limits

Weight %

Ti

C

Fe

N

Mo

O

Ni

H

Other

Titanium Grade 12

bal

0.08

0.3

0.03

0.2/0.4

0.25

0.6/0.9

0.015

0.4 total max

Titanium Grade 12 is similar to Grade 2 and Grade 3 except Grade 12 has the addition of Mo and Ni. These additions to Grade 12 offer a lower cost option than the Palladium bearing grades. Grade 12 has high strength, good heat and wear resistance and is highly weldable. Grade 12 is used for Chemical Processing, Power generation, Desalination, Marine Hydrocarbon processing and Mining

Typical Mechanical Properties

Material

Tensile Strength min

Yield Strength

Elongation in 2" (%)

ksi

Mpa

Max

Min

ksi

Mpa

Ksi

Mpa

Titanium CP Grade12
Annealed Sheet

70

483

50

345

-

-

18

as per MIL-T-9046J, AMS-T-9046, AMS 4901



Specifications
UNS R53401 
ASTM B265 Gr12 Sheet/plate
ASTM B337 Gr12 pipe (withdrawn)
ASTM B338 Gr12 heat exchange tube*
ASTM B348 Gr12 bar
ASTM B367 Gr12 castings
ASTM B381 Gr12 forgings
ASTM F467 Gr12 nuts
ASTM F468 Gr12 bolts 

 

 

Provide all grade of these alloy by different shape & size is Our expertise

For any inquiry & request, don't hesitate to contact us

 

Titanium Alloys - Ti0.3Mo0.8Ni Grade 12

 
 

Chemical Formula

Ti0.3Mo0.8Ni

Background

Highly weldable, near alpha titanium alloy exhibiting improved strength and optimum ASMA code design allowables at increased temperatures, combined with superior crevice corrosion resistance and excellent resistance under oxidising to mildly reducing conditions, especially chlorides.

Composition

Table 1. The composition of Ti3Al2.5.

 

Content

C

<0.08%

N2

<0.03%

Fe

<0.3%

H2

<0.015%

O2

<0.25%

Mo

0.2-0.4%

Ni

0.6-0.9%

Ti

Balance

Designations

Other designations for Ti3Al2.5 include:

•         ASTM B265 Gr12

•         ASTM B348 Gr12

•         ASTM B337 Gr12

•         ASTM B338 Gr12

•         ASTM B381 Gr12

•         ASTM B467 Gr12

•         ASTM F468 Gr12

Key Properties

Physical Properties

Table 2. Typical physical properties for Ti3Al2.5.

Property

Typical Value

Density g/cm3 (lb/ cu in)

4.51 (0.162)

Specific Heat (J/g.K)

0.54

Volume Electrical Resistivity ohm.cm (ohm.in)

41 (20)

Thermal Conductivity W/m.K (BTU/ft.h.°F)

21 (146)

Mean Co-Efficient of Thermal Expansion 0-100°C /°C

9.5x10-6

Beta Transus °C±15°C (°F)

888 (1630)

Mechanical Properties

Table 3. Typical mechanical properties for Ti3Al2.5 (data obtained for bar and plate 1” (25.4mm) thick, annealed.

Property

Minimum

Typical Value

Tensile Strength MPa (ksi)

483 (70)

607 (88)

0.2% Proof Stress MPa (ksi)

345 (50)

462 (67)

Elongation Over 2 Inches %

18

22

Reduction in Area (%)

25

 

Elastic Modulus GPa (msi)

 

103 (15)

Hardness BHn

 

103 (315)

Specified Bend Radius <0.070 in x Thickness

2.0

2.5

Welded Bend Radium x Thickness

14 (10)

 

Stress Rupture MPa (1000hr’s at (250°C)

297

 

Fabrication

•         Weldability – Good

•         Annealing – 732-816°C (1350-1500°F)

•         Stress Relief Annealing – 538-649°C (1000-1200°F), 1 hr, AC.

 

 

 

 

 

Availability:

 

 

  
 

TITANIUM GR12   Plate

TITANIUM GR12   Fittings

TITANIUM GR12   Tube / Pipe

 

 

 

 

 

TITANIUM GR12   Bar

TITANIUM GR12   Sheet

TITANIUM GR12   Coil /Strap

 

 

 

 

 

TITANIUM GR12   Fasteners / Flanges

TITANIUM GR12   Powder

TITANIUM GR12   Welding Product

 

 

Disclaimer
Every effort is made to ensure that technical specifications are accurate. However, technical specifications included herein should be used as a guideline only. All specifications are subject to change without notice.

Provide all grade of these alloy by different shape & size is Our expertise

For any inquiry & request, don't hesitate to contact us