nickel 200
Nickel 200 (UNS N02200)
Technical Data Sheet
Chemical Composition Limits |
|||||||
Weight% |
Ni |
Cu |
Fe |
Mn |
C |
Si |
S |
Nickel Alloy 200 |
99.0 min |
0.25 max |
0.40 max |
0.35 max |
0.15 max |
0.35 max |
0.01 max |
Nickel Alloy 201 |
99.0 min |
0.25 max |
0.40 max |
0.35 max |
0.02 max |
0.35 max |
0.01 max |
Commercially pure wrought Nickel with good mechanical properties over a wide range of temperature and excellent resistance to many corrosives, in particular hydroxides.
Good resistance to corrosion in acids and alkalis and is most useful under reducing conditions. Outstanding resistance to caustic alkalis up to and including the molten state. In acid, alkaline and neutral salt solutions the material shows good resistance, but in oxidizing salt solutions severe attack will occur. Resistant to all dry gases at room temperature and in dry chlorine and hydrogen chloride may be used in temperatures up to 550C. Resistance to mineral acids varies according to temperature and concentration and whether the solution is aerated or not. Corrosion resistance is better in de-aerated acid.
· Manufacture and handling of sodium hydroxide, particularly at temperature above 300C.
· Production of viscose rayon. Manufacture of soap.
· Analine hydrochloride production and in the chlorination of aliphatic hydrocarbons such as benzene, methane and ethane.
· Manufacture of vinyl chloride monomer.
· Reactors and vessels in which fluorine is generated and reacted with hydrocarbons.
Mechanical Property Requirements |
|||||
Ultimate Tensile |
Yield Strength (0.2% OS) |
Elong. |
R/A |
Hardness |
|
Cold Worked |
|||||
Min |
75 KSi |
50 KSi |
15 |
||
Max |
|||||
Min |
515 MPa |
345 MPa |
|||
Max |
|||||
Hot Worked |
|||||
Min |
55 KSi |
15 KSi |
40 |
||
Max |
|||||
Min |
380 MPa |
105 MPa |
|||
Max |
Rod |
ASTM B 160, ASME SB 160, DIN 17752, ISO 9723 |
Bar |
ASTM B 160, ASME SB 160, DIN 17752, ISO 9723 |
Pipe |
ASTM B 161, ASME SB161, ASTM B 163, ASME SB 163, ASTM B 725, ASME SB 725, ASTM B 730, ASME SB 730, ASTM B 751, ASME B 751, ASTM B775, ASME SB 775, ASTM B 829, ASME SB 829 DIN 17751, ISO 6207 |
Tube |
ASTM B 161, ASME SB161, ASTM B 163, ASME SB 163, ASTM B 725, ASME SB 725, ASTM B 730, ASME SB 730, ASTM B 751, ASME B 751, ASTM B775, ASME SB 775, ASTM B 829, ASME SB 829 DIN 17751, ISO 6207 |
Plate |
ASTM B 162, ASME SB 162, DIN 17750, ISO 6208 |
Sheet |
ASTM B 162, ASME SB 162, DIN 17750, ISO 6208 |
Strip |
ASTM B 162, ASME SB 162, DIN 17750, ISO 6208 |
Fittings |
ASTM B 366, ASME SB 366 |
Forgings |
ASTM B 546, ASME SB 564, ISO 9725, DIN 17754 |
Wire |
DIN 17753, ISO 9724 |
Other/Similar Specs |
UNS N02200, UNS N02201, BS HR 10, BS 3072, BS 3073, BS 3074, BS 3075, BS 3076, NA11, Werkstoff Nr. 2.4060, 2.4066, VNI200 |
Machinability Ratings
Carbide tools are suggested |
|
Machining Type |
Suggested starting rates are: |
Single Point turning : |
Roughing - 0.15" depth, 0.015"/rev feed -175 SFM |
Drilling : |
1/4" Dia hole - 0.004"/rev feed - 60 SFM |
Reaming : |
Feed - same as drilling - 100 SFM |
Side and Slot Milling : |
Roughing - 0.25" depth - 0.007"/tooth feed - 125SFM |
These rates are for carbide tools, |
Availability: |
|
|
|
NICKEL 200 Plate |
NICKEL 200 Fittings |
NICKEL 200 Tube / Pipe |
|
|
|
|
|
NICKEL 200 Bar |
NICKEL 200 Sheet |
NICKEL 200 Coil /Strap/Strip |
|
|
|
|
|
NICKEL 200 Fasteners / Flanges |
NICKEL 200 Powder |
NICKEL 200 Welding Product |
|
|
|
|
|
Provide all grade of these alloy by different shape & size is Our expertise
For any inquiry & request, don't hesitate to contact us
Disclaimer
Every effort is made to ensure that technical specifications are accurate. However, technical specifications included herein should be used as a guideline only. All specifications are subject to change without notice.