Titanium Alloys - Titanium / Palladium Alloys Grade 11 and Grade 17

 
 

Chemical Formula

Ti-Pd Alloys

Background

Ti-0.15Pd – Grade 11

This alloy has mechanical properties similar to commercially pure titanium grade 1, but with palladium added to enhance corrosion resistance in crevices and reducing acid chloride environments. As with grade 1, grade 11 has optimum ductility and cold formability. It has useful strength, high impact toughness and excellent weldability.

Ti-0.05Pd – Grade 17

Grade 17 is identical to grade 11, with the exception that the palladium added to improve corrosion resistance is less then with grade 11. Mechanical and physical properties, specifications and forms are all identical to grade 11.

The alloy composition differs by the reduction of Pd to 0.04-0.08%.

Titanium Ruthenium Alloys

The poor availability and high cost of palladium have led to the development of ruthenium as an alternative alloy addition to provide similar enhancement of corrosion resistance but at lower cost. The relevant ASTM Grade is 27 (CP Grade 1 + 0.1%Ru). Mechanical and physical properties are of the same order as described for grades 11 and 17.

Composition

Table 1. Composition of titanium-palladium alloys.

 

Content

 

Grade 11

Grade 17

O2

<0.18%

<0.18%

Fe

<0.20%

<0.20%

H2

<0.015%

<0.015%

C

<0.10%

<0.10%

N2

5.5-6.5%

5.5-6.5%

Pd

0.12-0.25%

0.04-0.08%

Ti

Balance

Balance

Designations

Other designations for Ti6Al2Sn4Zr2Mo include:

•         ASTM B265

•         ASTM B337 (Grade 11 only)

•         ASTM B338

•         ASTM B348

•         ASTM B363 (WPT)

•         ASTM B381

•         ASTM B861

•         ASTM B862

•         ASTM B863

•         See also ASTM list of B367 casting grades of palladium containing alloys for approximate equivalent specifications to the wrought grades above.

•         UNS R52250 Grade 11

•         UNS R52252 Grade 17

Key Properties

Physical Properties

Table 2. Typical physical properties for Ti6Al2Sn4Zr2Mo.

Property

Typical Value

Density g/cm3 (lb/ cu in)

4.51 (0.162)

Melting Range °C±15°C (°F)

1670 (3038)

Specific Heat J/kg.°C (BTU/lb/°F)

540 (0.129)

Volume Electrical Resistivity ohm.cm (ohm.in)

56 (22)

Thermal Conductivity W/m.K (BTU/ft.h.°F)

20.6 (143)

Mean Co-Efficient of Thermal Expansion 0-100°C /°C (0-212°F /°F)

8.6x10-6 (4.8)

Mean Co-Efficient of Thermal Expansion 0-300°C /°C (0-572°F /°F)

9.2x10-6 (5.1)

Beta Transus °C±15°C (°F)

888 (1630)

Mechanical Properties

Table 3. Typical mechanical properties for Ti6Al4V.

Property

Minimum

Typical Value

Tensile Strength MPa (ksi)

241 (35)

345 (50)

0.2% Proof Stress MPa (ksi)

172 (25)

221 (32)

Elongation Over 2 Inches %

25

37

Reduction in Area (%)

35

 

Elastic Modulus GPa (Msi)

 

103 (15)

Hardness (Bhn)

 

120

Specified Bend Radius <0.070 in x Thickness

 

1.5

Specified Bend Radius >0.070 in x Thickness

 

2.0

Welded Bend Radius x Thickness

 

2.0

Charpy, V-Notch Impact J (ft.lbs)

 

109 (80)

Fabrication

•         Weldability – Excellent

•         Forging – Rough 871°C (1600°F), finish 788-843°C (1450-1550°F)

•         Annealing – 704°C (1300°F) 2hr, AC

•         Stress Relief Annealing – 482-538°C (900-1o00°F) 45mins, AC

 

 

 

 

 

Availability:

 

 

 
 

TITANIUM GR11 & GR17   Plate

TITANIUM GR11 & GR17   Fittings

TITANIUM GR11 & GR17   Tube / Pipe

 

 

 

 

 

TITANIUM GR11 & GR17   Bar

TITANIUM GR11 & GR17   Sheet

TITANIUM GR11 & GR17   Coil /Strap

 

 

 

 

 

TITANIUM GR11 & GR17   Fasteners / Flanges

TITANIUM GR11 & GR17   Powder

TITANIUM GR11 & GR17   Welding Product

 

 

Disclaimer
Every effort is made to ensure that technical specifications are accurate. However, technical specifications included herein should be used as a guideline only. All specifications are subject to change without notice.