6105 aluminium alloy

 

6105 aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family (6000 or 6xxx series). It is one of the least common of the alloys in this series. While most wrought aluminium alloys are covered by multiple standards (from any mixture of ASTMENISO, and national standard bodies), 6105 is only dealt with in ASTM B221: Standard Specification for Aluminum and Aluminum-Alloy Extruded Bars, Rods, Wire, Profiles, and Tubes. It is formed by extrusion, and supplied in heat treated form. It can alternately referred to by the UNS designation A96105.

Chemical composition

The alloy composition of 6105 aluminium is:

·         Aluminium: 97.2 to 99.0%

·         Chromium: 0.1% max

·         Copper: 0.1% max

·         Iron: 0.35% max

·         Magnesium: 0.45 to 0.8%

·         Manganese: 0.1% max

·         Silicon: 0.6 to 1.0%

·         Titanium: 0.1% max

·         Zinc: 0.1% max

·         Residuals: 0.15% max

Properties

Typical material properties for 6105 aluminum alloy include:

·         Density: 2.69 g/cm3, or 168 lb/ft3.

·         Young's modulus: 70 GPa, or 10 Msi.

·         Ultimate tensile strength: 190 to 270 MPa, or 28 to 39 ksi.

·         Yield strength: 120 to 260 MPa, or 17 to 38 ksi.

·         Thermal Expansion: 21.8 μm/m-K.

 

Availability

Provide all grade of these alloy by different shape & size is Our expertise

For any inquiry & request, don't hesitate to contact us

 Disclaimer
Every effort is made to ensure that technical specifications are accurate. However, technical specifications included herein should be used as a guideline only. All specifications are subject to change without notice.